Characterization of low-cost Brazilian resin composites submitted to tooth brushing

Abstract: This in vitro study aimed to evaluate surface microhardness, roughness, color, gloss and topography of low-cost Brazilian resin composites, compared with an international one. All 120 samples (8mm ø x 2mm height) were prepared and divided into 5 groups: Ultrafill (Biodinâmica), Llis (FGM), Fill Magic (Coltene), Applic (Makira), and Filtek Z250XT (3M Oral Care). Surface microhardness (KHN) (n=10) was analyzed at two time periods: before and after simulated tooth brushing (STB). Other standardized samples of each group (n=10) were analyzed for surface roughness (Ra), color (ΔL, Δa, Δb, ΔE, ΔE00) and gloss unit (GU) at the same two periods. The topography of non-brushed and brushed samples of each group (n=4) was evaluated by scanning electron microscopy. Data were analyzed statistically by two-way repeated measures ANOVA with Bonferroni post-hoc test (KHN, Ra, GU), and one-way ANOVA with Tukey post-hoc test (ΔL, Δa, Δb, ΔE, ΔE00) (α=0.05). Topographic images were submitted to descriptive analysis. The low-cost Brazilian resin composites investigated were compared with the international one and revealed: lower KHN, regardless of before or after STB; statistically similar Ra before STB, except Ultrafill, which presented higher values; lower Ra after STB, except Ultrafill, which presented statistically similar values; statistically similar color change in ΔL, Δa, Δb parameters; statistically similar color change in ΔE, ΔE00 parameters, except Fill Magic, which presented lower values; lower gloss before STB; lower gloss after STB, except Ultrafill, which presented statistically similar values. In a situation of scarce resources, low-cost Brazilian composites might be an acceptable cost-effective restorative alternative.

Assessment of a novel bleaching agent formula containing 35% hydrogen peroxide and titanium tetrafluoride: an in vitro study

Abstract: This study developed experimental gels containing titanium tetrafluoride (TiF4) combined with commercial 35% hydrogen peroxide (HP), and evaluated bleaching efficacy and pH of the gels, and mineral content and morphology of enamel submitted to these treatments. In phase-1, different stock gels mixed with TiF4 were combined with HP. In phase-2, the selected gels were tested on enamel/dentin specimens (n=8): HP; HP and Natrosol+TiF4 (HPnT); HP and Natrosol+Chemygel+TiF4 (HPncT); HP and Aristoflex+TiF4 (HPaT). Bleaching was performed in four sessions (3x15min-application/session). Color (CIEL*a*b*) and whiteness index (WID) were measured after each session, whereas whiteness index differences (ΔWID), color alteration (CIELab-ΔE, CIEDE2000-ΔE00), enamel morphology and pH, at end of bleaching therapy. The change in Knoop microhardness (ΔKHN) was compared before and after bleaching. Data were analyzed by two-way repeated measures ANOVA and Bonferroni (CIEL*, a*, b*), one-way ANOVA and Tukey (ΔWID, ΔE, ΔE00), and LSD (ΔKHN) tests (α=5%). SEM and pH measurements were submitted to descriptive analysis. No differences were observed in lightness (L*) or WID among the groups (p > 0.05), but HP exhibited lower b* values (p<0.05), higher ΔWID than HPnT, and the highest ΔE among the groups (p < 0.05). No differences in ΔE00 were observed between HP and HPncT (p > 0.05), and HPncT showed higher ΔKHN than HP (p < 0.05). HP presented pH values closer to neutral (6.9), whereas experimental agents showed acidic pH values (2.3-3.9). No morphological changes were observed in HP or HPncT groups. HPncT was able to bleach the enamel and maintain enamel microhardness and surface integrity, even at low pH.